YUHONG GROUP CO.,LIMITED

86-574-88013900

Home > Recommended
Product Categories
Online Service

Factory Supply Factory price for Din Forged Stainless Steel Flange ASTM A182 F904L Lap Joint Flange 12" 150# supply to Bangladesh Exporter

  • Product Detail
  • Product Tags
  • Buyer Reviews

welcomes all buyers to visit our company and inspect. Let us cooperate hand in hand to make a good future. for ASTM A182 F904L Lap Joint Flange,Steel Flanges ANSI Class 150 A182 F904L,Weld Neck Flanges ASTM A 182 F904L Stainless Steel WN. Innovation and Win-Win business". Welcome to visit our site and tend not to be reluctant to communicate with us. Are you prepared? ? ? Allow us to go!!!

Factory Supply Factory price for Din Forged Stainless Steel Flange ASTM A182 F904L Lap Joint Flange 12" 150# supply to Bangladesh Exporter

ASTM B 677 NO8904 / 904L , ASTM B366 NO8904 / 904L, 1.4539, Stainless Steel Seamless Tube

ASTM A182 F904L Flange

 
904L Stainless Steel Pipes and Tubes
904L is a non-stabilised low carbon high alloy austenitic stainless steel. The addition of copper to this grade gives it greatly improved resistance to strong reducing acids, particularly sulphuric acid. It is also highly resistant to chloride attack - both pitting / crevice corrosion and stress corrosion cracking. This grade is non-magnetic in all conditions and has excellent weldability and formability. The austenitic structure also gives this grade excellent toughness, even down to cryogenic temperatures. 904L does have very substantial contents of the high cost ingredients nickel and molybdenum. Many of the applications in which this grade has previously performed well can now be fulfilled at lower cost by duplex stainless steel 2205 (S31803 or S32205), so it is used less commonly than in the past.
ASTM B 677 NO8904 / 904L , ASTM B366 NO8904 / 904L, 1.4539, Stainless Steel Seamless Tube

 

904L Stainless Steel Pipes and Tubes Product Range 
904L Stainless Steel Pipes and Tubes Specifications: ASTM A/ASME SA 269/677 904L Stainless Steel Pipes and Tubes Sizes (Seamless): 1/2" NB - 8" NB
904L Stainless Steel Pipes and Tubes Sizes (ERW): 1/2" NB - 24" NB
904L Stainless Steel Pipes and Tubes Sizes (EFW): 6" NB - 100" NB  
904L Stainless Steel Pipes and Tubes Wall Thickness available:
Schedule 5S - Schedule XXS (heavier on request)

 904L Stainless Steel Pipes and Tubes Other Materials Testing:
 NACE MR0175, H2 SERVICE, OXYGEN SERVICE, CRYO SERVICE, etc.
904L Stainless Steel Pipes and Tubes Dimensions:
 All Pipes is manufactured and inspected/tested to the relevant standards including ASTM, ASME and API etc.

Key Properties
These properties are specified for flat rolled product (plate, sheet and coil) in ASTM B625. Similar but not necessarily identical properties are specified for other products such as pipe, tube and bar in their respective specifications.
Composition
Table 1. Composition ranges for 904L grade of stainless steels.


Grade

C

Mn

Si

P

S

Cr

Mo

Ni

Cu

904L

min.
max.

-
0.020

-
2.00

-
1.00

-
0.045

-
0.035

19.0
23.0

4.0
5.0

23.0
28.0

1.0
2.0

                     

Mechanical Properties
Table 2. Mechanical properties of 904L grade stainless steels.


Grade

Tensile Strength (MPa) min

Yield Strength 0.2% Proof (MPa) min

Elongation (% in 50mm) min

Hardness

Rockwell B (HR B)

Brinell (HB)

904L

490

220

35

70-90 typical

-

Rockwell Hardness value range is typical only; other values are specified limits.

Physical Properties
Table 3. Typical physical properties for 904L grade stainless steels.


Grade

Density
(kg/m3)

Elastic Modulus
(GPa)

Mean Co-eff of Thermal Expansion (m/m/C)

Thermal Conductivity
(W/m.K)

Specific Heat 0-100C
(J/kg.K)

Elec Resistivity
(n.m)

0-100C

0-315C

0-538C

At 20C

At 500C

904L

8000

200

15

-

-

13

-

500

850

Grade Specification Comparison
Table 4. Grade specifications for 904L grade stainless steels.


Grade

UNS No

Old British

Euronorm

Swedish SS

Japanese JIS

BS

En

No

Name

904L

N08904

904S13

-

1.4539

X1NiCrMoCuN25-20-5

2562

-

These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.

Possible Alternative Grades
Table 5. Possible alternative grades to 904L stainless steel.

 


Grade

Why it might be chosen instead of 904L

316L

A lower cost alternative, but with much lower corrosion resistance.

6Mo

A higher resistance to pitting and crevice corrosion resistance is needed.

2205

A very similar corrosion resistance, with the 2205 having higher mechanical strength, and at a lower cost to 904L. (2205 not suitable for temperatures above 300C.)

Super duplex

Higher corrosion resistance is needed, together with a higher strength than 904L.

 

Corrosion Resistance
Although originally developed for its resistance to sulphuric acid it also has a very high resistance to a wide range of environments. A PRE of 35 indicates that the material has good resistance to warm sea water and other high chloride environments. High nickel content results in a much better resistance to stress corrosion cracking than the standard austenitic grades. Copper adds resistance to sulphuric and other reducing acids, particularly in the very aggressive "mid concentration" range.
In most environments 904L has a corrosion performance intermediate between the standard austenitic grade 316L and the very highly alloyed 6% molybdenum and similar "super austenitic" grades.
In aggressive nitric acid 904L has less resistance than molybdenum-free grades such as 904LL and 310L.
For maximum stress corrosion cracking resistance in critical environments the steel should be solution treated after cold work.
Heat Resistance
Good resistance to oxidation, but like other highly alloyed grades suffers from structural instability (precipitation of brittle phases such as sigma) at elevated temperatures. 904L should not be used above about 400C.
Heat Treatment
Solution Treatment (Annealing) - heat to 1090-1175C and cool rapidly. This grade cannot be hardened by thermal treatment.
Welding
904L can be successfully welded by all standard methods. Care needs to be taken as this grade solidifies fully austenitic, so is susceptible to hot cracking, particularly in constrained weldments. No pre-heat should be used and in most cases post weld heat treatment is also not required. AS 1554.6 pre-qualifies Grade 904L rods and electrodes for welding of 904L.
Fabrication
904L is a high purity, low sulphur grade, and as such will not machine well. Despite this the grade can be machined using standard techniques.
Bending to a small radius is readily carried out. In most cases this is performed cold. Subsequent annealing is generally not required, although it should be considered if the fabrication is to be used in an environment where severe stress corrosion cracking conditions are anticipated.

 

 

Applications


 

  • Typical applications include
  • Processing plant for sulphuric, phosphoric and acetic acids
  • Pulp and paper processing
  • Components in gas scrubbing plants
  • Seawater cooling equipment
  • Oil refinery components
  • Wires in electrostatic precipitators

904L
Chemical Composition %

C Cr Cu Mn Mo Ni P S Si
Max     Max     Max Max Max
0.02 19.0-23.0 1.0-2.0 2.0 4.0-5.0 23.0-28.0 0.045 0.035 1.0


AVAILABILITY
Seamless Pipe 1/2" W
SPECIFICATIONS
ASTM B677, B366
ASME SB677, SB366

 


DESIGN FEATURES
Good resistance to pitting and crevice corrosion.
Very good resistance to stress corrosion cracking.
Good resistance to intergranular corrosion.
Good formability and weldability.
Maximum service temperatures of
450 deg.C. (824 deg.F).

TYPICAL APPLICATIONS
Production and transport of sulfuric acid
Metal pickling in sulfuric acid
Production and concentration of phosphoric acid
Use in seawater, brackish water, condensers, heat exchangers and pipe work in general
Paper and allied industries
Gas washing
Chemical and pharmaceutical industries

TENSILE REQUIREMENTS
Tensile Strength (KSI) 70
Yield Strength (KSI) 25
KSI can be converted to MPA (Megapascals) by multiplying by 6.895.

 

Some of the quality tests carried out by us includes:

Corrosion Test Conducted only when specially requested by the client
Chemical Analysis Test done as per required quality standards
Destructive / Mechanical Testing Tensile | Hardness | Flattening | Flare | Flange
Reverse-bend and Re. flat tests Carried out in full compliance with relevant standards & ASTM A-450 and A-530 norms, which ensures trouble-free expansion, welding & use at customers end
Eddy Current Testing Done to detect homogeneities in subsurface by using Digital Flaw-mark Testing System
Hydrostatic Testing 100% Hydrostatic Testing carried out according to ASTM-A 450 norms for checking tube leakage, and biggest pressure we can support 20Mpa/7s .
Air Under Pressure Test To check any evidence of air leakage
Visual Inspection After passivation, every single length of tubes & pipes is subjected to thorough visual inspection by trained staff for detecting surface flaws & other imperfections


Supplementary Testing : Apart from the above mentioned tests, we also carry out on the manufactured products supplementary testing. The tests conducted under this include:

  • Eddy Current Testing
  • O.P Testing
  • Radiography Testing
  • Corrosion Testing
  • Micro Testing
  • Macro Testing
  • IGC Testing
  • Ultrasonic testing
  • Liquid Penetrate testing

"To be the stage of realizing dreams of our employees! To build a happier, more united and more professional team! To reach a mutual benefit of our customers, suppliers, the society and ourselves for ASTM A182 F904L Lap Joint Flange 12" 150#. The product will supply to all over the world, such as: Romania,Faroe Islands,Comoros. Customer's satisfaction is always our quest creating value for customers is always our duty a long term mutual-beneficial business relationship is what we are doing for. We are an absolutely reliable partner for you in China. Of course other services like consulting can be offered too.

Email To This Supplier

Your message must be between 20-8000 characters

YOU MAY LIKE
  • ANSI LAP JOINT FLANGE

    Specifications ANSI LAP JOINT FLANGE 1 SLIP ON WELD NECK BLIND LAP JOINT THREAD SOCKET WELD FLANGE 2 1 2 48 INCH 3 ANTIRUST OIL or BLACK ANSI LAP JOINT FLANGE 1 ANSI FLANGE FORGED CARBON STEEL FLANGE 2 Type Plate Slip on Welding Neck Thread Socket Weld Blind 3 Size 1 2 48 inch 4 Material Carbon steel A105 SS400 SF440 RST37 2 S235JRG2 P250GH C22 8 Stainless Steel F304 F304L F316 F316L 316Ti 5 Surface Treatment Anti rust Oil

    Ask PriceClick for details

  • A105 flange forged flange class1200 lap joint flange

    OUR FACTORY PRODUCTS OF FLANGE THE MAIN TYPE AND MATERIALS OF OUR

    Ask PriceClick for details

  • ANSI B16.5 flange lap joint flange 150lb rf flange

    OUR PRODUCT OF ANSI FLANGE THE MAIN TYPE AND MATERIALS OF OUR FLANGE The main products of our company

    Ask PriceClick for details

  • Stainless Steel Lap Joint Flange

    Specifications Stainless Steel Lap Joint Flange 1 Standard BS NPT DIN GOST 2 Certification ISO 9001 2008 API 3 Size 20 300mm 1 Stainless Steel Lap Joint Flange Introduction

    Ask PriceClick for details

  • OEM high quality cnc machining forging steel lap joint flange

    OEM high quality cnc machining forging steel lap joint flange Product Description Capabilities 1 Vcnc milling the workable length 1 1000mm the workable

    Ask PriceClick for details

  • Carbon Steel Fitting Lap Joint Flange, ASTM 300lb, 600lb

    Model NO Lap Joint Flange Type Lap Joint Flange Structure

    Ask PriceClick for details