Quality comes first; service is for ASME SA213 TP310S Stainless Steel Seamless Tube,Heat Exchanger Tube A213 TP310S,Stainless Steel Boiler Tube DIN 17456 1.4845. We warmly welcome friends from all walks of existence to cooperate with us.
Grade 310 is a medium carbon austenitic stainless steel, for high temperature applications such as furnace parts and heat treatment equipment. It is used at temperatures up to 1150°C in continuous service, and 1035°C in intermittent service. Grade 310S is a low carbon version of grade 310.
Applications of Grade 310/310S Stainless Steel
Typical Applications Grade 310/310S is used in fluidised bed combustors, kilns, radiant tubes, tube hangers for petroleum refining and steam boilers, coal gasifier internal components, lead pots, thermowells, refractory anchor bolts, burners and combustion chambers, retorts, muffles, annealing covers, saggers, food processing equipment, cryogenic structures.
Properties of Grade 310/310S Stainless Steel
These grades contain 25% chromium and 20% nickel, making them highly resistant to oxidation and corrosion. Grade 310S is a lower carbon version, less prone to embrittlement and sensitisation in service. The high chromium and medium nickel content make these steels capable for applications in reducing sulphur atmospheres containing H2S. They are widely used in moderately carburising atmospheres, as encountered in petrochemical environments. For more severe carburising atmospheres other heat resisting alloys should be selected. Grade 310 is not recommended for frequent liquid quenching as it suffers from thermal shock. The grade is often used in cryogenic applications, due to its toughness and low magnetic permeability.
In common with other austenitic stainless steels, these grades cannot be hardened by heat treatment. They can be hardened by cold work, but this is rarely practiced.
Chemcial Composition of Grade 310/310S Stainless Steel.
The chemical composition of grade 310 and grade 310S stainless steel are summarised in the following table.
Table 1. Chemical composition % of grade 310 and 310S stainless steel
|Carbon||0.25 max||0.08 max|
|Manganese||2.00 max||2.00 max|
|Silicon||1.50 max||1.50 max|
|Phosphorus||0.045 max||0.045 max|
|Sulphur||0.030 max||0.030 max|
|Chromium||24.00 – 26.00||24.00 – 26.00|
|Nickel||19.00 – 22.00||19.00 – 22.00|
Mechanical Properties of Grade 310/310S Stainless Steel
The mechanical properties of grade 310 and grade 310S stainless steel are summarised in the following table.
Table 2. Mechanical properties of of grade 310/310S stainless steel
|Mechanical Properties||310/ 310S|
|Grade 0.2 % Proof Stress MPa (min)||205|
|Tensile Strength MPa (min)||520|
|Elongation % (min)||40|
|Hardness (HV) (max)||225|
Physical Properties of Ferritic Stainless Steel
The physical properties of grade 310 and grade 310S stainless steel are summarised in the following table.
Table 3. Physical properties of grade 310/310S stainless steel
|Electrical Resistivity||25°C||0.78||Micro ohm.m|
|Modulus of Elasticity||20°C||200||GPa|
|Relative Magnetic Permeability||1.02|
|Coefficient of Expansion||0-100°C||15.9||/°C|
Fabrication of Grade 310/310S Stainless Steel
Fabrication Grades 310/310S are forged in the temperature range 975 – 1175°C. Heavy work is carried out down to 1050°Cand a light finish is applied to the bottom of the range. After forging annealing is recommended to relieve all stresses from the forging process. The alloys can be readily cold formed by standard methods and equipment.
Machinability of Grade 310/310S Stainless Steel
Machinability Grades 310/310SS are similar in machinability to type 304. Work hardening can be a problem and it is normal to remove the work hardened layer by using slow speeds and heavy cuts, with sharp tools and good lubrication. Powerful machines and heavy, rigid tools are used.
Heat Treatment of Grade 310/310S Stainless Steel
Heat Treatment Type 310/310S are solution annealed by heating to temperature range 1040 -1065°C, holding at temperature until thoroughly soaked, then water quenching.
Heat Resistance of Grade 310/310S Stainless Steel
Grades 310/310S have good resistance to oxidation in intermittent service in air up to 1035°Cand 1050°C in continuous service. The grades are resistant to oxidation, sulphidation and carburisation.
Available Forms of Grade 310/310S Stainless Steel
Austral Wright Metals can supply these grades as plate, sheet and strip, bar and rod, seamless tube and pipe, welded tube and pipe, forgings and forging billet, tube and pipe fittings, wire. Corrosion Resistance Grade 310/310S is generally not used for corrosive liquid service, although the high chromium and nickel content give corrosion resistance superior to grade 304. The alloy does not contain molybdenum, so pitting resistance is quite poor. Grade 310/310S will be sensitised to intergranular corrosion after service at temperatures in range 550 – 800°C. Chloride stress corrosion cracking may take place in corrosive liquids containing chlorides at temperatures exceeding 100°C.
"So as to provide you with ease and enlarge our business, we even have inspectors in QC Crew and guarantee you our best company and solution for ASME SA213 TP310S Stainless Steel Seamless Tube. The product will supply to all over the world, such as: France Metropolitan,Falkland Islands (Malvinas),Palau. Our company has built stable business relationships with many well-known domestic companies as well as oversea customers. With the goal of providing high quality products to customers at low cots we've been committed to improving its capacities in research development manufacturing and management. We have honored to receive recognition from our customers. Till now we have now passed ISO9001 in 2005 and ISO/TS16949 in 2008. Enterprises of "quality of survival the credibility of development" for the purpose sincerely welcome domestic and foreign businessmen to visit to discuss cooperation.